Petro Rabigh PE FS250B
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Rabigh Refining & Petrochemical Co. |
| Trademark: | Petro Rabigh PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mGzaWW_Petro-Rabigh-PE-FS250B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FS250B is a linear low density polyethylene resin intended for cast film applications. This resin has good flow characteristics for easy processing. Films made from this resin exhibit excellent transparency, and good toughness properties. Applications
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.921 | g/cm³ | ASTM D792A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.2 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 20 µm | 150 | MPa | |
| 1% Secant, TD : 20 µm | 150 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 20 µm | 50.0 | MPa | |
| TD : Break, 20 µm | 30.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 20 µm | 620 | % | |
| TD : Break, 20 µm | 940 | % | |
| Dart Drop Impact (20 µm) | 75 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 20 µm | 60 | g | |
| TD : 20 µm | 240 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 122 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 20.0 µm) | 145 | ASTM D2457 | |
| Haze (20.0 µm) | 0.60 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 220 to 280 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMILITE® PL-1621 (Machining) | Sumitomo Bakelite Co., Ltd. | Phenolic | SUMILITE® |
| Hapflex™ 1036-5 | Hapco Inc. | TP, Unspecified | Hapflex™ |
| HiFill® HDPE TM40 | Techmer Engineered Solutions | HDPE | HiFill® |
| PETILEN I10-19T | PETKIM Petrokimya Holding A.S. | LDPE | PETILEN |
| Rotuba CAP CP801 (16% Plasticizer) | Rotuba Extruders, Inc. | CAP | Rotuba CAP |