PENTAMID A SK H RC schwarz
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTAMID A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mGyCrw_PENTAMID-A-SK-H-RC-schwarz.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Normal viscosity, heat stabilised polyamide 66, short cycle time, Recompound |
| General Information | |
|---|---|
| Additive |
|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.13 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction | 2.0 | -- | % | ISO 294-4 |
| Flow direction | 1.9 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 7.7 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.5 | -- | % | ISO 62 |
| Viscosity Number | 130 | -- | cm³/g | ISO 307 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 165 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3200 | 1300 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2 | |||
| Yield | 75.0 | 50.0 | MPa | ISO 527-2 |
| Fracture | -- | 50.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | |||
| Yield | 3.5 | 15 | % | ISO 527-2 |
| Fracture | -- | 50 | % | ISO 527-2 |
| Flexural Modulus | 3100 | -- | MPa | ISO 178 |
| Flexural Stress | 125 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 75.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Dielectric Strength (1.00 mm) | 27 | -- | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.60 | -- | IEC 60250 | |
| Comparative Tracking Index | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | V-2 | -- | UL 94 | |
| 3.20 mm | V-2 | -- | UL 94 |
| Additional Information |
|---|
| 干燥 ISO Description: PA66, MHRC, 14-030The value listed as Melting Point, ISO 3146, was tested in accordance with ISO 11357. |
| 调节后的 ISO Description: PA66, MHRC, 14-030Tensile Strain at Break, ISO 527: >50% |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.14 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 260 - 285 | °C | |
| Middle Temperature | 275 - 290 | °C | |
| Front Temperature | 275 - 285 | °C | |
| Processing (Melt) Temp | 280 | °C | |
| Mold Temperature | 80.0 | °C | |
| Injection Pressure | 60.0 | MPa | |
| Holding Pressure | 36.0 | MPa | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REPOL® AER003N | Reliance Industries Limited | PP Random Copolymer | REPOL® |
| Chemlon® 60Z | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| EPLAMID 6 GFT 20 NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 6 | EPLAMID 6 |
| Latilub 66-01M G/50 | LATI S.p.A. | Nylon 66 | Latilub |
| Karina IVORY PVC COMPOUND 90901-35/ 1-D-AC-AS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |