TRANSMARE® 19HT30-0.002
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Transmare Compounding B.V. |
| Trademark: | TRANSMARE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mGp1Ro_TRANSMARE-19HT30-0-002.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRANSMARE® 19HT30-0.002 is a 30% standard (gray) talc filled polypropylene homopolymer for injection molding purposes with high stiffness and good flow. Not suitable for light colors. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 20 | g/10 min | |
| 230°C/5.0 kg | 90 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 74 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 4.00 mm | 35.0 | MPa | |
| Break, 4.00 mm | 30.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 4.00 mm | 3.0 | % | |
| Break, 4.00 mm | 10 | % | |
| Flexural Modulus 1 | 4300 | MPa | ISO 178 |
| Flexural Stress 2 | 54.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.5 | kJ/m² | ISO 179/A |
| Notched Izod Impact Strength (23°C) | 2.6 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 118 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 73.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 154 | °C | ISO 306/A |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premier HD00354 | Premier Polymers, LLC. | HDPE | Premier |
| TYRIL™ 905 | Trinseo | SAN | TYRIL™ |
| Hostacom TKG 324N Black | LyondellBasell Industries | PP Copolymer | Hostacom |
| Petrotene® PP A3 T10 NTLA010 PH374 MSP | Petropol Industry and Trade of Polymers LTDA | PP Homopolymer | Petrotene® PP |
| Sylvin 9077-70 White 1463 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |