RTP 262
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mEvfeL_RTP-262.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18mm, injection molding | 1.5 | % | ASTM D955 |
| 6.35mm, injection molding | 2.0 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 1.5 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 4130 | MPa | ASTM D638 |
| Tensile Strength | 65.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield, Injection Molded) | 10 | % | ASTM D638 |
| Flexural Modulus (Injection Molded) | 2760 | MPa | ASTM D790 |
| Flexural Strength (Injection Molded) | 83.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm, Injection Molded) | 43 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 1100 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, injection molded | 193 | °C | ASTM D648 |
| 1.8 MPa, unannealed, injection molded | 74.0 | °C | ASTM D648 |
| CLTE - Flow | 4.3E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+6 | ohms | ASTM D257 |
| Volume Resistivity | 10 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Flammibility, UL 94, was tested in accordance with RTP Company methods.Static Decay MIL-PRF-81705D, FTMS-4046.1: 2 sec |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 274 - 293 | °C | |
| Middle Temperature | 274 - 293 | °C | |
| Front Temperature | 274 - 293 | °C | |
| Mold Temperature | 66.0 - 107 | °C | |
| Injection Pressure | 69.0 - 124 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premier PPCR-2020 | Premier Polymers, LLC. | PP Copolymer | Premier |
| BJB Polyurethane TC-800 A/B | BJB Enterprises, Inc. | PUR, Unspecified | BJB Polyurethane |
| Fainplast PVC RK 317/UV | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Kelon® B H CETG/300 | LATI S.p.A. | Nylon 6 | Kelon® B |
| POCAN® T 7331 000000 | LANXESS GmbH | PBT+PET | POCAN® |