Miramid® VE40C

Category:	Nylon 6 , Polyamide 6
Manufacturer:	BASF Leuna GmbH
Trademark:	Miramid®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	mErzTE_Miramid-VE40C.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Miramid® VE40C is a Polyamide 6 (Nylon 6) material filled with 40% glass fiber. It is available in Europe for injection molding.

Important attributes of Miramid® VE40C are:

Flame Rated

Chemical Resistant

Crystalline

Fast Molding Cycle

Good Stiffness

Typical applications include:

Engineering/Industrial Parts

Automotive

Construction Applications

Electrical/Electronic Applications

Sporting Goods

General Information
Filler / Reinforcement	Glass Fiber, 40% Filler by Weight
Additive	Mold Release
Features	Crystalline Fast Molding Cycle Fuel Resistant Good Flow Good Stability Good Stiffness Grease Resistant High Rigidity Oil Resistant Solvent Resistant
Uses	Automotive Applications Building Materials Electrical/Electronic Applications Engineering Parts Machine/Mechanical Parts Sporting Goods
Forms	Granules
Processing Method	Injection Molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1)

Physical	Dry	Conditioned	Unit	Test Method
Density	1450	--	kg/m³	ISO 1183 ¹
Water Absorption				ISO 62 ²
Saturation	5.3	--	%
Equilibrium	1.4	--	%
Viscosity number	145	--	cm³/g	ISO 307, 1157, 1628 ³

Hardness	Dry	Conditioned	Unit	Test Method
Ball Indentation Hardness	250	--	MPa	ISO 2039-1

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile modulus	12000	8000	MPa	ISO 527-2 ⁴
Tensile Stress (Break)	195	130	MPa	ISO 527-2 ⁵
Tensile Strain (Break)	3.0	5.0	%	ISO 527-2 ⁶
Flexural Stress ⁷	300	180	MPa	ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Charpy notched impact strength				ISO 179/1eA ⁸
-30°C	12.0	--	kJ/m²
23°C	14.0	23.0	kJ/m²
Charpy impact strength				ISO 179/1eU ⁹
-30°C	65.0	--	kJ/m²
23°C	95.0	105	kJ/m²

Thermal	Dry	Conditioned	Unit	Test Method
Deflection Temperature Under Load				ISO 75-2 ¹⁰
0.45 MPa	215	--	°C
1.8 MPa	210	--	°C
Continuous Use Temperature				ISO 2578
-- ¹¹	115	--	°C
-- ¹²	130	--	°C
-- ¹³	180	--	°C
Melting Temperature (DSC)	220	--	°C	ISO 3146

Electrical	Dry	Conditioned	Unit	Test Method
Volume resistivity	1.0E+13	1.0E+10	ohms·m	IEC 60093 ¹⁴
Dielectric Constant (1 MHz)	3.90	6.00		IEC 60250
Dissipation Factor (1 MHz)	0.015	0.15		IEC 60250 ¹⁵
Comparative tracking index	550	--		IEC 60112 ¹⁶

Flammability	Dry	Conditioned	Unit	Test Method
Burning Rate (1.00 mm)	< 100	--	mm/min	FMVSS 302
Flame Rating (1.50 mm)	HB	--		UL 94
Burning Behav. at thickness h (1.50 mm)	HB	--		ISO 1210 ¹⁷
Glow Wire Flammability Index (1.00 mm)	650	--	°C	IEC 60695-2-12

Injection	Dry	Unit
Processing (Melt) Temp	260 to 290	°C
Mold Temperature	80.0 to 120	°C

Note Message
1 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
2 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
3 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
4 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
5 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
6 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
7 .	Typical values for uncoloured product at 23°C and 50% relative humidity
8 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
9 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
10 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
11 .	Temperature index at loss of 50% tensile strength, 20000h
12 .	Temperature index at loss of 50% tensile strength, 5000h
13 .	Short time
14 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
15 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
16 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
17 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.

Resin Grade	Manufacturer	Category	Trademark
Ultradur® B 4300 G3	BASF Corporation	PBT	Ultradur®
Advanced Composites ATX832D	Advanced Composites, Inc.	TPO	Advanced Composites
Borealis PP RF365MO	Borealis AG	PP, Unspecified	Borealis PP
Dugdale PVC Dynamic PVC Nitrile Flexible Compound	Dugdale Plc	PVC, Flexible	Dugdale PVC
NILAMID® XT1 GF30	Nilit Plastics	PPA	NILAMID®