PULSE™ 2300 PT
| Category: | PC+ABS , PC/ABS Engineering Resin |
| Manufacturer: | Trinseo |
| Trademark: | PULSE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mDGdmK_PULSE-2300-PT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PULSE™ 2300 PT is a PC/ABS Engineering Resin product. It is available in North America. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 1.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.15 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 51.7 | MPa | |
| Break | 48.3 | MPa | |
| Tensile Elongation (Break) | 80 | % | ASTM D638 |
| Flexural Modulus | 2240 | MPa | ASTM D790 |
| Flexural Strength | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -29°C | 480 | J/m | |
| 23°C | 640 | J/m | |
| Instrumented Dart Impact | ASTM D3763 | ||
| -29°C, Total Energy | 59.9 | J | |
| 23°C, Total Energy | 54.2 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 124 | °C | |
| 1.8 MPa, Unannealed | 107 | °C | |
| CLTE - Flow (-29 to 100°C) | 7.2E-5 | cm/cm/°C | ASTM D696 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Novalloy-S S69P1 | Daicel Polymer Ltd. | PC+ABS | Novalloy-S |
| Axiall PVC 7181 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| DAPCO™ 3100FR | Cytec Industries Inc. | Epoxy | DAPCO™ |
| Globalene® 6331-11 | Lee Chang Yung Chemical Industry Corp. | PP Homopolymer | Globalene® |
| Moplen HP500L | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |