Celstran® POM-GF25-04 AF3001
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celstran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mCxu6K_Celstran-POM-GF25-04-AF3001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Material code according to ISO 1043-1: POM Acetal copolymer reinforced with 25 weight percent long glass fibers. The fibers are chemically coupled to the POM matrix. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long. Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Application field: Functionial/structural parts for automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.59 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10300 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 177 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.4 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 9190 | MPa | ISO 178 |
| Flexural Stress (23°C) | 265 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 35 | kJ/m² | ISO 179/1eA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 180 - 195 | °C | |
| Middle Temperature | 190 - 200 | °C | |
| Front Temperature | 195 - 205 | °C | |
| Nozzle Temperature | 195 - 205 | °C | |
| Processing (Melt) Temp | 195 - 205 | °C | |
| Mold Temperature | 70.0 - 110 | °C | |
| Injection Pressure | 60.0 - 120 | MPa | |
| Injection Rate | Moderate | ||
| Holding Pressure | 60.0 - 120 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Feed Temperature: 20 to 50°CZone 4 Temperature: 195 to 205°CManifold Temperature: 195 to 205°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE PCG07 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| TPX® RT31XB | Mitsui Chemicals, Inc. | PMP Copolymer | TPX® |
| Arnite® AV2 370 XL | DSM Engineering Plastics | PET | Arnite® |
| HONES® PPS HS-G40-6 | Guangdong Shunde Hones Polymer Material Co., Ltd. | PPS | HONES® |
| POLYFLON™ M-18F | Daikin Fluorochemicals (China) Co., Ltd. | PTFE | POLYFLON™ |