DIC.PPS Z-200-E5
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | DIC Corporation |
| Trademark: | DIC.PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mCmWMp_DIC-PPS-Z-200-E5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.3 | % | |
| Across Flow | 1.5 | % | |
| Water Absorption (23°C, 24 hr) | 0.030 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ASTM D638 |
| Tensile Strength | 70.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 50 | % | ASTM D638 |
| Flexural Modulus | 2900 | MPa | ASTM D790 |
| Flexural Strength | 110 | MPa | ASTM D790 |
| Compressive Strength | 100 | MPa | ASTM D695 |
| Poisson's Ratio | 0.38 | ||
| Flexural Elongation at Break | > 50 | % | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 80 | J/m | ASTM D256 |
| Unnotched Izod Impact | 2000 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 160 | °C | |
| 1.8 MPa, Unannealed | 105 | °C | |
| CLTE | ASTM D696 | ||
| Flow : -30 to 100°C | 4.5E-5 | cm/cm/°C | |
| Transverse : -30 to 100°C | 4.5E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm) | 16 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.40 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 2.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 290 to 320 | °C | |
| Middle Temperature | 290 to 320 | °C | |
| Front Temperature | 290 to 320 | °C | |
| Mold Temperature | 120 to 150 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP PHC31-81 | Saudi Basic Industries Corporation (SABIC) | PP Impact Copolymer | SABIC® PP |
| Sicoklar E51.10 | Ravago Group | PC | Sicoklar |
| APEX® 74-8208-A | Teknor Apex Company | PVC, Flexible | APEX® |
| Hostalen PP HF500B | LyondellBasell Industries | PP Homopolymer | Hostalen |
| Polifil® Nylon 627 | The Plastics Group | Nylon 66 | Polifil® Nylon |