SILVER® PA640
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Guangdong Silver Age Sci & Tech. Co., Ltd |
| Trademark: | SILVER® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mC6Frw_SILVER-PA640.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SILVER® PA6/ PA66 is applied to many fields, such as electronic facility, electronic tool and power facility. In addition, the custom—made products should be developed by buyers‘ requirements in order to meet special usage. Modified PA66 |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 80.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 12 | % | ASTM D638 |
| Flexural Modulus 3 | 2400 | MPa | ASTM D790 |
| Flexural Strength 4 | 120 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Area) (23°C) | 4.00 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 120 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 250 to 270 | °C |
| Note Message | |
|---|---|
| 1 . | 10 mm/min |
| 2 . | 10 mm/min |
| 3 . | 5.4 mm/min |
| 4 . | 5.4 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-201-G10 211 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| Xuchuan XCW-8065DY | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Elastane™ 4720-70A | Technical Polymers, LLC | TPU-Polyester | Elastane™ |
| Globalprene® 3522 | Lee Chang Yung Chemical Industry Corp. | SBS | Globalprene® |
| Osterlene® PPR02CLNX | Osterman & Company | PP Random Copolymer | Osterlene® |