Adell PS IF-110
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Adell Plastics, Inc. |
| Trademark: | Adell PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mBwGzB_Adell-PS-IF-110.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Adell PS IF-110 is a flame retardant impact polystyrene concentrate. IF-110 is a cost effective material to be used in high impact polystyrene applications where UL rating of V-0 is critical. The concentrate is typically mixed with HIPS at a ratio of two parts of base resin with one part of IF-110 to obtain a V-0 rating at 1/16" for the molded product. The physical properties of the concentrate have been engineered to produce molded parts from HIPS and the concentrate blend that have properties similar to those molded of HIPS. The property data of test bars produced from two parts HIPS and one part IF-110 is shown on this datasheet. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/1.2 kg) | 5.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 27.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 40 | % | ISO 527-2 |
| Flexural Modulus | 2000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 100 | kJ/m² | ISO 180/1U |
| Gardner Impact | 8.00 | J | ASTM D3029 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SCR5-2015 | Spartech Polycom | PP Copolymer | Spartech |
| JSR EPR EP57P | JSR Corporation | EPDM | JSR EPR |
| POCAN® B 3217 XF 000000 | LANXESS GmbH | PBT | POCAN® |
| POCAN® A 3131 000000 | LANXESS Corporation | PBT+ASA | POCAN® |
| NORYL™ SE1GFN3 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |