SABIC® PP 518A
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | SABIC Americas, Inc. |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mBZkaA_SABIC-PP-518A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Provisional - PP Homopolymer for fiber applications PP 518A is a PP homopolymer with broad molecular weight distribution intended for fiber extrusion applications. PP 518A has following features:
Typical Applications PP 518A is particularly suitable for producing bulk continuous filament (BCF), continuous filament (CF) and staple fiber yarns for carpet pile and upholstery. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 0.905 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 25 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, Injection Molded) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, Injection Molded) | 32.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield, Injection Molded) | 12 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (Injection Molded) | 1550 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Injection Molded) | 30 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 118 | °C | ASTM D648 |
| Vicat Softening Temperature | 152 | °C | ASTM D1525 2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 210 - 250 | °C |
| Extrusion instructions |
|---|
| Lower processing temperature are possible with this material and will result in better long term heat aging. |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 标准 B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POWERSIL® 402 A/B | Wacker Chemie AG | Silicone | POWERSIL® |
| Ravago Compounds PP-6062 | Ravago Manufacturing Americas, LLC | PP Impact Copolymer | Ravago Compounds |
| Nylene® 9643 | Custom Resins Group | Nylon 66/6 | Nylene® |
| Bakelite® PF 6507 | Hexion Inc. | Phenolic | Bakelite® |
| ESENTTIA 05C05 | Polipropileno del Caribe S.A. | PP Impact Copolymer | ESENTTIA |