CALIBRE™ 603-6
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m9U4pZ_CALIBRE-603-6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 603-6 Polycarbonate Resin is a branched polycarbonate resin specially designed for multi-wall sheet extrusion. CALIBRE 603-6 offers a high melt strength to calibrate effectively a wide range of multi-wall sheet structures from low to high complexity, such as seven wall sheet. CALIBRE 603-6 offers a wider processing window than CALIBRE 503-5 and is likewise specially designed to give excellent sheet surface quality at high line speeds with a reduced tendency to display chatter marks. CALIBRE 603-6 contains a UV absorber additive, but sheets for outdoor applications require a protective UV-absorbing cap layer. It is recommended to coextrude a 50 micron thick cap layer from CALIBRE 320UV. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183/B |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.15 | % | |
| Equilibrium, 23°C, 50% RH | 0.32 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2350 | MPa | ISO 527-2/50 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 62.0 | MPa | |
| Break | 66.0 | MPa | |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2400 | MPa | ISO 178 |
| Flexural Stress 2 | 93.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 16 | kJ/m² | |
| 23°C | 55 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 15 | kJ/m² | |
| 23°C | 80 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 145 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 126 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 142 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 150 | °C | ISO 306/B50 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (2.00 mm, Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 3 | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Glow Wire Flammability Index 4 | IEC 60695-2-12 | ||
| 1.00 mm | 900 | °C | |
| 2.00 mm | 875 | °C | |
| 3.00 mm | 875 | °C | |
| Glow Wire Ignition Temperature 5 | IEC 60695-2-13 | ||
| 1.00 mm | 800 | °C | |
| 2.00 mm | 775 | °C | |
| 3.00 mm | 775 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ISO 489 | |
| Transmittance | 86.0 to 90.0 | % | ASTM D1003 |
| Haze | 1.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 4 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 5 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene MBW1444 | Teknor Apex Asia Pacific PTE. LTD. | PP, Unspecified | Sinpolene |
| NaturePlast PEVI 001 | NaturePlast | HDPE | NaturePlast |
| Firestone CLM200-001 | Firestone Textiles Company | Nylon 6 | Firestone |
| LNP™ VERTON™ RX89047 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ VERTON™ |
| Durethan® DP AKV 50 HR H2.0 901510 | LANXESS GmbH | Nylon 66 | Durethan® |