Next Nylon 66 Prime Series PGHSLR30-01BK
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 66 Prime Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m96sYh_Next-Nylon-66-Prime-Series-PGHSLR30-01BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA66 Glass Fiber Reinforced Heat stabilized & Hydrolysis resistant Black compound Product Applications Typical Application include automotive radiator mounting frame, header tanks cooling and heating radiator system etc Benefits Good chemical resistance, Fuel /oil resistance, grease resistance with high strength |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.36 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 0.30 | -- | % | ASTM D955 |
| Transverse flow | 0.80 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 1.9 | -- | % | ASTM D570 |
| Saturation 1 | 6.1 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| Class m | 110 | -- | ASTM D785 | |
| Class r | 120 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9200 | 7200 | MPa | ASTM D638 |
| Tensile Strength | 180 | 130 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | 5.0 | % | ASTM D638 |
| Flexural Modulus | 8300 | -- | MPa | ASTM D790 |
| Flexural Strength | 245 | 210 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | 140 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 260 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 253 | -- | °C | ASTM D648 |
| Melting Temperature | 262 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+17 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength | 38 | 32 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 450 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 This grade is not suitable for food contact, medical devices or toy applications |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 - 270 | °C | |
| Middle Temperature | 270 - 280 | °C | |
| Front Temperature | 280 - 290 | °C | |
| Mold Temperature | 65.0 - 85.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-201-G0 291 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| Sarlink® TPV 2655 | Teknor Apex Company | TPV | Sarlink® TPV |
| YUNGSOX® PP 3504 | Formosa Polypropylene | PP Impact Copolymer | YUNGSOX® PP |
| CERTENE™ PBM-1NB | Muehlstein | PP Impact Copolymer | CERTENE™ |
| Elastron® G G400.A52.T | Elastron USA, Inc. | SEBS | Elastron® G |