LNP™ THERMOTUF™ DF004PSI compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ THERMOTUF™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m8zBS1_LNP-THERMOTUF-DF004PSI-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Glass Reinforced Polycarbonate. High Flow Ductile, High Chemical Resistance |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.33 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 10.0 | cm³/10min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow | 0.30 to 0.50 | % | |
| Across Flow | 0.30 to 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6100 | MPa | ASTM D638 |
| -- | 5960 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 99.0 | MPa | ASTM D638 |
| Break | 99.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.9 | % | ASTM D638 |
| Break | 2.9 | % | ISO 527-2/5 |
| Flexural Modulus 4(50.0 mm Span) | 5380 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 50.0 mm Span) | 147 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 16 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength (23°C) | 48 | kJ/m² | ISO 179/2U |
| Notched Izod Impact (23°C) | 160 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 630 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 130 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 126 | °C | |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 2.5E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.0E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 280 to 300 | °C | |
| Nozzle Temperature | 285 to 305 | °C | |
| Processing (Melt) Temp | 285 to 310 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Back Pressure | 0.100 to 0.300 | MPa | |
| Screw Speed | 50 to 90 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Syncure™ V0022G RoHS Natural | PolyOne Corporation | XLPE | Syncure™ |
| Network Polymers LLDPE 11 0218 | Network Polymers, Inc. | LLDPE | Network Polymers LLDPE |
| EPO-TEK® M10-D | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Hostaform® C 13031 LS | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| KEBAFORM® C 274 VT | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |