EVAL™ C109
| Category: | EVOH , Ethylene Vinyl Alcohol |
| Manufacturer: | Kuraray Co., Ltd. |
| Trademark: | EVAL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m8E3E9_EVAL-C109.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
35 mol% Ethylene Vinyl Alcohol Copolymer C109B - Pellets are lubricated to facilitate material feeding into extruder |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 9.3 | g/10 min | |
| 210°C/2.16 kg | 21 | g/10 min | |
| Ethylene Content | 35.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 94 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 68.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 6.0 | % | ISO 527-2 |
| Flexural Modulus | 4800 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Permeability | ISO 14663-2 | ||
| 20°C, 0% RH | 5.9E-3 | cm³·mm/m²/atm/24 hr | |
| 20°C, 65% RH | 0.012 | cm³·mm/m²/atm/24 hr | |
| 20°C, 85% RH | 0.038 | cm³·mm/m²/atm/24 hr | |
| Water Vapor Transmission Rate 1(40°C, 90% RH) | 0.94 | g·mm/m²/atm/24 hr | ASTM E96 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 1.0 | kJ/m² | ISO 179/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 53.0 | °C | ISO 11357-2 |
| Melting Temperature | 177 | °C | ISO 11357 |
| Peak Crystallization Temperature | 154 | °C | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | Procedure E |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AIE PET 40G6F | Asia International Enterprise (Hong Kong) Limited | PET | AIE PET |
| DJSilicone NE-171 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| KRATON® D1113 P | Kraton Polymers LLC | SIS | KRATON® |
| KumhoSunny ABS HAG5210 | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |
| MACOMASS PP MM-PP HF 25 | MACOMASS Verkaufs AG | PP Homopolymer | MACOMASS PP |