Order Products : sales@su-jiao.com
GAPEX® RPP20DA
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Ferro Corporation |
| Trademark: | GAPEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m7AnB0_GAPEX-RPP20DA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GAPEX® RPP20DA is a Polypropylene material filled with 20% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of GAPEX® RPP20DA are:
Typical application of GAPEX® RPP20DA: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 to 0.40 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 72 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 40.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.5 | % | ASTM D638 |
| Flexural Modulus | 3650 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 59.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 32 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 190 | J/m | ASTM D256 |
| Gardner Impact (3.18 mm) | 0.226 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 146 | °C | |
| 1.8 MPa, Unannealed | 116 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 221 to 238 | °C | |
| Middle Temperature | 227 to 243 | °C | |
| Front Temperature | 232 to 260 | °C | |
| Nozzle Temperature | 232 to 260 | °C | |
| Processing (Melt) Temp | 221 to 238 | °C | |
| Mold Temperature | 37.8 to 65.6 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.138 to 0.345 | MPa | |
| Cushion | 5.08 to 12.7 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MBA PP 2182 | MBA Polymers | PP Copolymer | MBA PP |
| CGPC PVC R-11X MI Injection | China General Plastics Corporation | PVC, Flexible | CGPC PVC |
| Huafon JF-W-3400 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| LG PVC LS080S | LG Chem Ltd. | PVC, Unspecified | LG PVC |
| POLYasa 2410F | Polykemi AB | ASA | POLYasa |