Synthos EPS® 0513FR/CZ
| Category: | PS (EPS) , Expanded Polystyrene |
| Manufacturer: | Synthos S.A. |
| Trademark: | Synthos EPS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m74SQf_Synthos-EPS-0513FR-CZ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Synthos EPS®/CZ types 0513FR, 0514FR 0822FR, 1640FR and 2040FR are self-extinguishing expandable polystyrene EPS with low content of pentane. The materials are formed by spherical polystyrene particles that contain a flame retardant system (content of HBCD < 0,5%) and a hydrocarbon blowing agent. Their surface is treated against gluing during processing and the formation of electrostatic charge. Due to the content of halogenated flame retardant and the residual blowing agent, the product is unsuitable for objects intended for direct contact with food. Synthos EPS® 0513FR/CZ (Koplen 0513FR) and Synthos EPS® 0514FR/CZ (Koplen 0514FR) is mainly used for production of shaped parts with wall thickness above 10 mm (e.g. shipping packaging for glass and electrical goods, building bricks, floor and roof shaped parts); production of smaller blocks with higher density or cutted profiles. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Density 1 | 0.03 to 0.04 | g/cm³ | Internal Method |
| Moisture Content | < 10000 | ppm | Internal Method |
| Particle Size - >95% between | 500 to 1250 | µm | Internal Method |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Reaction to Fire | |||
| -- | B1 | DIN 4102 | |
| -- | Class E | EN 13501-1 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blowing Agent | < 5.5 | wt% | Internal Method |
| Note Message | |
|---|---|
| 1 . | The typical bulk density indicates values obtained during single-step pre-foaming on continuous pre-foaming devicesLower values of bulk density can be achieved only after multiple pre-expansion. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 3400 G-430 | RTP Company | LCP | RTP |
| Shandong Aobang TPU-Capro 90-A | Shandong Aobang Chemical Technology Co.,Ltd. | TPU-Capro | Shandong Aobang TPU-Capro |
| TEREZ PA 6 7400 GK 50 | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| Topolymer® 5211-901E | Dongguan Top Polymer Enterprise | TPE | Topolymer® |
| Electrafil® TPU G/CF40 | Techmer Engineered Solutions | TPU, Unspecified | Electrafil® |