Generic ABS+Acrylic
| Category: | ABS+Acrylic , Acrylonitrile Butadiene Styrene + Acrylic (PMMA) |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m6Yeo7_Generic-ABS-Acrylic.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic ABS+Acrylic This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 to 1.11 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 5.0 to 33 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 0.40 to 0.55 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 98 to 119 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 34.5 to 45.2 | MPa | ASTM D638 |
| Flexural Modulus (23°C) | 2060 to 2360 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 68.5 to 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 to 240 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 82.0 to 89.6 | °C | ASTM D648 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TABOREN PR 58 T 20 | SILON s.ro | PP Copolymer | TABOREN |
| CarmelStat™ CS 1118 | Carmel Olefins Ltd. | PP, Unspecified | CarmelStat™ |
| Evermore PUR SA-2018MP | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| Hifax BB222GC | LyondellBasell Industries | TPO (POE) | Hifax |
| Karina WHITE PVC COMPOUND 833D10/184-AY-IS-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |