Michilene F8100
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | API Polymers, Inc. |
| Trademark: | Michilene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m6UpU3_Michilene-F8100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Michilene F8100 is a Polypropylene Homopolymer (PP Homopolymer) product. It is available in North America. Primary characteristic: homopolymer. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.903 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.3 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 33.1 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 12 | % | ASTM D638 |
| Flexural Modulus - Tangent | 1380 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 32 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 98.9 | °C | |
| 1.8 MPa, Unannealed | 60.0 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 216 | °C | |
| Middle Temperature | 216 | °C | |
| Front Temperature | 210 | °C | |
| Nozzle Temperature | 204 | °C | |
| Processing (Melt) Temp | 216 | °C | |
| Mold Temperature | 26.7 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XAREC™ C132 | Idemitsu Kosan Co., Ltd. | SPS | XAREC™ |
| apigo® CA 150 | API SpA | TPO (POE) | apigo® |
| KumhoSunny PET HEG3620FG | Shanghai KumhoSunny Plastics Co., Ltd. | PET | KumhoSunny PET |
| Capilene® W 50 | Carmel Olefins Ltd. | PP Homopolymer | Capilene® |
| Silastic® Q7-4850 | Dow Corning Corporation | Silicone | Silastic® |