TEKAFIN™ PB60G10
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | TEKAFIN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m5WKdN_TEKAFIN-PB60G10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PB60G10 is GF10% reinforced Compounded-PP. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.988 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 49.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | < 10 | % | ASTM D638 |
| Flexural Modulus 3 | 1960 | MPa | ASTM D790 |
| Flexural Strength 4 | 68.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 49 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 140 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 190 to 210 | °C | |
| Middle Temperature | 200 to 230 | °C | |
| Front Temperature | 200 to 230 | °C | |
| Nozzle Temperature | 210 to 230 | °C | |
| Processing (Melt) Temp | 210 to 230 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 3.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Witcom PA6 4C+G-XHI | Witcom Engineering Plastics B.V. | Nylon 6 | Witcom PA6 |
| Colorite G Series 7011G-015 | Colorite Polymers | PVC, Flexible | Colorite G Series |
| DOMAMID® 66M40 | DOMO Engineering Plastics SPA | Nylon 66 | DOMAMID® |
| Karina RED PVC COMPOUND -E711D42/158-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| TECACOMP® PA66 GF30 TF15 HI black 3366 | Ensinger GmbH | Nylon 66 | TECACOMP® |