| ES-215 SERIES HIGH-TEMP SURFACE COATS were developed to meet the requirements of the aircraft and aerospace industry for use which demands higher temperature applications greater than 170°C/350°F. These surface coats have proven in tests that their compatibility with prepreg systems produce excellent surface conditions cured under heat and vacuum bagging. The thermo-cycling of these systems exhibit a great degree of high physical stability when used in tooling and composite fabrication. These systems are versatile in that they can be used in RHL and IHL heat environment applications. These qualities allow the fabricator a single system which will sustain both specifications in deference to using two different systems. These systems are hygienically safe for shop usage as they do not contain MDA OR VCHD. Use in conjunction with any ADTECH high-temp laminating resin. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Density | 1.23 | g/cm³ | ASTM D1895 |
| Moisture Absorption | 0.16 | % | ASTM D570 |
| Viscosity | |||
| Hardener | 50 to 60 | mPa·s | |
| Resin | Thixotropic |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Strength - Ultimate | 150 | MPa | ASTM D965 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tack Free Time | 5.0 to 6.0 | hr |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Work Life | 3.0 to 3.7 | hr |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 88 to 90 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4450 | MPa | ASTM D638 |
| Tensile Strength (Break) | 34.0 | MPa | ASTM D638 |
| Flexural Modulus | 2950 | MPa | ASTM D790 |
| Flexural Strength (Break) | 58.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 190 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 194 | °C | |
| 1.8 MPa, Unannealed | 187 | °C | |
| CLTE - Flow | 2.9E-5 | cm/cm/°C | ASTM D696 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 1.0 Mix Ratio by Weight: 17 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 4.8 | ||
| Shelf Life | |||
| -- 1 | 52 | wk | |
| -- 2 | 100 | wk | |
| Thermoset Mix Viscosity (25°C) | 100000 to 150000 | cP | ASTM D2393 |
| Demold Time | 960 to 1400 | min |
| Note Message | |
|---|---|
| 1 . | Resin in original nopened container |
| 2 . | Hardener in original nopened container |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravalene CR H 2544 | Ravago Group | HDPE | Ravalene |
| Andur 2-90 AP/Curene® 442 | Anderson Development Company | PUR-Ether/TDI | Andur |