Akulon® K223-TP4
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Akulon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m3KY5Z_Akulon-K223-TP4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Akulon® K223-TP4 is a Polyamide 6 (Nylon 6) material. It is available in Europe or North America for injection molding. Important attributes of Akulon® K223-TP4 are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.07 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.7 | -- | % | |
| Flow | 1.4 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 8.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.3 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2000 | 625 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 50.0 | 30.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.0 | 30 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | > 50 | > 50 | % | ISO 527-2 |
| Flexural Modulus | 1600 | -- | MPa | ISO 178 |
| Flexural Stress | 65.0 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 18 | 25 | kJ/m² | |
| 23°C | 65 | 75 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 130 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 55.0 | -- | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | |||
| Flow | 1.2E-4 | -- | cm/cm/°C | |
| Transverse | 1.2E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 5.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 27 | 20 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 3.10 | 10.0 | ||
| 1 MHz | 2.70 | 3.50 | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 3.0E-3 | 0.16 | ||
| 1 MHz | 0.016 | 0.10 | ||
| Comparative Tracking Index | -- | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification (1.60 mm) | HB | -- | IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.50 mm | 700 | -- | °C | |
| 2.00 mm | 700 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 1.50 mm | 725 | -- | °C | |
| 2.00 mm | 725 | -- | °C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 230 to 235 | °C | |
| Middle Temperature | 235 to 250 | °C | |
| Front Temperature | 240 to 260 | °C | |
| Nozzle Temperature | 240 to 270 | °C | |
| Processing (Melt) Temp | 240 to 275 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp DBS8602 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Chiao Fu PBT PBT819B30 NAT | Chiao Fu Enterprises Co., Ltd. | PBT | Chiao Fu PBT |
| Elastollan® C 98 A | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| Hylon® N1000THLUV2 | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| Sylvin 5132-86 Clear Green 3166 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |