POLYfill PPC T5020
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Polykemi AB |
| Trademark: | POLYfill |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m340D3_POLYfill-PPC-T5020.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Mineral reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.0 to 1.3 | % | |
| Flow | 1.0 to 1.3 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 25.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 8.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 1900 | MPa | ISO 178 |
| Flexural Stress | 38.0 | MPa | ISO 178 |
| Scratch Resistance 1 | ISO 1518/D65 | ||
| 10 N Fine Structure | 3.30 | dL | |
| 10 N Rough Structure | 3.80 | dL | |
| 20 N Fine Structure | 4.40 | dL | |
| 20 N Rough Structure | 5.30 | dL |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 2.0 | kJ/m² | |
| 23°C | 7.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 2 | |||
| 0.45 MPa, Unannealed | 110 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 60.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 140 | °C | ISO 306/A50 |
| -- | 58.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | Test performed on black plaques with fine (Standex MT9078) and rough (Standex MT11435) structure |
| 2 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| QAMAR FC21HS | SPDC Ltd. | LLDPE | QAMAR |
| Ad-Tech Epoxy ES-219 | Ad-Tech Plastic Systems Corp. | Epoxy | Ad-Tech Epoxy |
| EverGlide® SG3220 | Polymer Dynamix | PEEK | EverGlide® |
| HAIPLEN H50 C4 | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| LNP™ LUBRICOMP™ RCP36 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |