4PROP® 9C12420 IUV
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | 4Plas |
| Trademark: | 4PROP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m21ODN_4PROP-9C12420-IUV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4PROP 9C12420 IUV is a MFI 5 20% Chemically Coupled Glass Fibre Impact Modified, UV Stabilised Copolymer Polypropylene |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 4250 | MPa | ISO 527-2/5 |
| Tensile Stress (Break, 23°C) | 7.00 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 5.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 10 | kJ/m² | ISO 180/1A |
| 23°C | 20 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature 1 | 165 | °C | ISO 11357 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 - 240 | °C | |
| Mold Temperature | 20.0 - 50.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 40.0 - 80.0 | MPa | |
| Screw Speed | 400 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 20 - 60 °CBack Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Delta ATL C27-UV | Delta Polymers | Acetal (POM) Copolymer | Delta |
| HONES® PA66 G35 | Guangdong Shunde Hones Polymer Material Co., Ltd. | Nylon 66 | HONES® |
| Hostacom X M3 N07 | LyondellBasell Industries | PP Copolymer | Hostacom |
| LNP™ LUBRICOMP™ DFL22E compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |
| LNP™ LUBRICOMP™ KFL36 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |