Durethan® BKV 215 H2.0 901510

Category:	Nylon Copolymer , Polyamide Copolymer
Manufacturer:	LANXESS GmbH
Trademark:	Durethan®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	m0fwNs_DurethanBKV215H20901510.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
PA 6-Copolymer, 15 % glass fibers, injection molding, improved impact strength, heat-aging stabilized

General Information
Filler / Reinforcement	Glass fiber reinforced material, 15% filler by weight
Additive	heat stabilizer
Features	Copolymer Impact resistance, good Thermal Stability
Agency Ratings	EC 1907/2006 (REACH)
Processing Method	Injection molding

Physical	Dry	Conditioned	Unit	Test Method
Density (23°C)	1.17	--	g/cm³	ISO 1183
Apparent Density	0.60	--	g/cm³	ISO 60
Molding Shrinkage				ISO 2577
Vertical flow direction : 280°C, 2.00mm ¹	0.60	--	%	ISO 2577
Vertical flow direction : 120°C, 4 hours, 2.00mm ²	0.10	--	%	ISO 2577
Flow direction : 280°C, 2.00mm ³	0.60	--	%	ISO 2577
Flow direction : 120°C, 4 hours, 2.00mm ⁴	0.10	--	%	ISO 2577
Water Absorption				ISO 62
Saturated, 23°C	7.0	--	%	ISO 62
Equilibrium, 23°C, 50% RH	2.0	--	%	ISO 62

Hardness	Dry	Conditioned	Unit	Test Method
Ball Indentation Hardness	120	55.0	MPa	ISO 2039-1

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus (23°C)	4500	2300	MPa	ISO 527-2/1
Tensile Stress (Break, 23°C)	85.0	55.0	MPa	ISO 527-2/5
Tensile Strain (Break, 23°C)	4.5	15	%	ISO 527-2/5
Flexural Modulus ⁵(23°C)	4200	2300	MPa	ISO 178/A
Flexural Stress				ISO 178/A
3.5% strain, 23°C	125	55.0	MPa	ISO 178/A
23°C ⁶	135	75.0	MPa	ISO 178/A
Flexural Strain at Flexural Strength ⁷(23°C)	5.5	8.5	%	ISO 178/A

Additional Information	Dry	Conditioned		Test Method
ISO Shortname	PA 6/66-HI, GHR, 14-040, GF15	--		ISO 1874

Injection	Dry	Unit	Test Method
Residual Moisture Content	0.030 - 0.12	%	Karl Fisher

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength				ISO 179/1eA
-30°C	10	12	kJ/m²	ISO 179/1eA
23°C	20	35	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength				ISO 179/1eU
-30°C	80	80	kJ/m²	ISO 179/1eU
23°C	70	95	kJ/m²	ISO 179/1eU
Notched Izod Impact				ISO 180/1A
-30°C	10	10	kJ/m²	ISO 180/1A
23°C	20	35	kJ/m²	ISO 180/1A
Unnotched Izod Impact Strength				ISO 180/1U
-30°C	65	60	kJ/m²	ISO 180/1U
23°C	60	90	kJ/m²	ISO 180/1U
Multi-Axial Instrumented Impact Energy				ISO 6603-2
-30°C	4.50	--	J	ISO 6603-2
23°C	11.0	--	J	ISO 6603-2
Multi-Axial Instrumented Impact Peak Force				ISO 6603-2
-30°C	775	--	N	ISO 6603-2
23°C	1440	--	N	ISO 6603-2

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	205	--	°C	ISO 75-2/B
1.8 MPa, not annealed	175	--	°C	ISO 75-2/A
8.0 MPa, not annealed	60.0	--	°C	ISO 75-2/C
Vicat Softening Temperature	200	--	°C	ISO 306/B120
Melting Temperature ⁸	214	--	°C	ISO 11357-3
Linear thermal expansion coefficient				ISO 11359-2
Flow : 23 to 55°C	4.0E-5	--	cm/cm/°C	ISO 11359-2
Lateral : 23 to 55°C	1.7E-4	--	cm/cm/°C	ISO 11359-2

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating				UL 94
1.60 mm	HB	--		UL 94
3.20 mm	HB	--		UL 94
Glow Wire Flammability Index (2.00 mm)	650	--	°C	IEC 60695-2-12
Oxygen Index ⁹	22	--	%	ISO 4589-2

Injection	Dry	Unit	Test Method
Drying Temperature - Dry Air Dryer	80.0	°C
Drying Time - Dry Air Dryer	2.0 - 6.0	hr
Processing (Melt) Temp	260 - 290	°C
Mold Temperature	80.0 - 100	°C

Note Message
1 .	60x60x2mm, 80°C MT, 600 bar
2 .	60x60x2mm
3 .	60x60x2mm, 80°C MT, 600 bar
4 .	60x60x2mm
5 .	2.0 mm/min
6 .	2.0 mm/min
7 .	2 mm/min
8 .	10°C/min
9 .	Procedure A

Resin Grade	Manufacturer	Category	Trademark
RAMOFIN PPH343T4BK11	Polyram Ram-On Industries	PP Homopolymer	RAMOFIN
Bapolan® PS6078-G	Bamberger Polymers, Inc.	PS (HIPS)	Bapolan®
Hyundai EP PA6 LS345	HYUNDAI EP Co., Ltd.	Nylon 6	Hyundai EP PA6
POLYfill PP HIP16020FCF	Polykemi AB	PP, Unspecified	POLYfill
Sylvin 802-88 Clear Black 285	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin