BESTNYL SI00VI12BEWX
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Triesa Plastics |
| Trademark: | BESTNYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | m0aTFL_BESTNYL-SI00VI12BEWX.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6 grey high viscosity lubrified with V-0 free halogen quality, normally used in electrical appliances or pipes, for its easy extrusion as well as injection and mould release combine with excellent flame resistance. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 3.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.0 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 1.3 | % | ISO 62 |
| Humidity - Pellets | 0.20 | % | ISO 1110 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Test | OK | IEC 60695-2-13 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ISO 527-2 |
| Tensile Stress | 80.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 25 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 185 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 70.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | > 200 | °C | ISO 306 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 230 to 250 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3970H | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Spartech Polycom E65090 | Spartech Polycom | PVC, Unspecified | Spartech |
| THERMOLAST® K TF8BNA (Series: FC/AP) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Exact™ 4056 | ExxonMobil Chemical | Plastomer | Exact™ |
| LNP™ THERMOCOMP™ Lexan_LGK3020 compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOCOMP™ |