AT 418
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Celanese EVA Performance Polymers |
| Trademark: | AT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lx0nSO_AT-418.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A low density polyethylene resin well suited for extrusion coating and lamination applications. This resin has excellent adhesion and low neck-in at high speeds. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.916 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A | 94 | ||
| Shore D | 47 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 9.50 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 500 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 202 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 89.0 | °C | ASTM D1525 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 280 to 320 | °C | |
| Maximum Line Speed | 7.6 | m/sec | |
| Minimum Coating Thickness 3 | 5.0 | µm |
| Note Message | |
|---|---|
| 1 . | Type IV, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| 3 . | 3 lb/ream |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® GS25-66 22L-NBK1 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| TRIBOCOMP® PPS GF30 TS0 | EPIC Polymers | PPS | TRIBOCOMP® |
| LUVOCOM® 105-8763 | Lehmann & Voss & Co. | TPE | LUVOCOM® |
| Plasmer 5065N/1002 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |
| Kanghui KH2090 | Yingkou Kanghui Petrochemical Co., LTD. | PBT | Kanghui |