AT 525
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Celanese EVA Performance Polymers |
| Trademark: | AT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lwZvgP_AT-525.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A high strength resin, recommended for shrink films and general purpose packaging. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 0.45 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 35 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 35 µm, Blown Film | 230 | MPa | |
| 1% Secant, TD : 35 µm, Blown Film | 270 | MPa | |
| Tensile Strength 1 | ASTM D882A | ||
| MD : Yield, 35 µm, Blown Film | 13.0 | MPa | |
| TD : Yield, 35 µm, Blown Film | 13.0 | MPa | |
| MD : Break, 35 µm, Blown Film | 29.0 | MPa | |
| TD : Break, 35 µm, Blown Film | 22.0 | MPa | |
| Tensile Elongation 2 | ASTM D882A | ||
| MD : Break, 35 µm, Blown Film | 400 | % | |
| TD : Break, 35 µm, Blown Film | 610 | % | |
| Dart Drop Impact (35 µm, Blown Film) | 74 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 99.8 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 35.0 µm, Blown Film) | 50 | ASTM D2457 | |
| Haze (35.0 µm, Blown Film) | 9.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 to 215 | °C |
| Note Message | |
|---|---|
| 1 . | 500 mm/min |
| 2 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® STAMAX 40YM240 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® STAMAX |
| Vydyne® R535J BK0701 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Abstron KU600 | Bhansali Engineering Polymers Limited | ABS | Abstron |
| AKROMID® B3 GF 35 black (2196) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| LNP™ THERMOCOMP™ RF006ESZ compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |