Amilan® CM1046
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Toray Resin Company |
| Trademark: | Amilan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lvDyfQ_Amilan-CM1046.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Amilan® CM1046 is a Polyamide 6 (Nylon 6) product. It can be processed by blow molding and is available in Asia Pacific, Europe, or North America. |
| General Information | |
|---|---|
| Uses |
|
| Processing Method |
|
| Part Marking Code |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.13 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 1.8 | -- | % | |
| Saturation, 23°C | 11 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 119 | -- | ISO 2039-2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress | ISO 527-2 | |||
| -40°C | 110 | 100 | MPa | |
| 23°C | 75.0 | 35.0 | MPa | |
| 80°C | 25.0 | 20.0 | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Break, -40°C | 3.0 | 3.0 | % | |
| Break, 23°C | 50 | 50 | % | |
| Break, 80°C | 50 | 50 | % | |
| Flexural Modulus | ISO 178 | |||
| -40°C | 3800 | 3600 | MPa | |
| 23°C | 2500 | 800 | MPa | |
| 80°C | 700 | 300 | MPa | |
| Flexural Stress | ISO 178 | |||
| -40°C | 135 | 125 | MPa | |
| 23°C | 100 | 40.0 | MPa | |
| 80°C | 40.0 | 25.0 | MPa | |
| Taber Abrasion Resistance (1000 Cycles) | 3.00 to 4.00 | -- | mg | ISO 9352 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | -- | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -40°C | 5.5 | 40 | kJ/m² | |
| 23°C | No Break | -- |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 182 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | -- | °C | ISO 75-2/A |
| Melting Temperature | 225 | -- | °C | DSC |
| CLTE - Flow | 8.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+14 to 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Electric Strength | 20 | -- | kV/mm | IEC 60243-1 |
| Dielectric Constant 1 | IEC 60250 | |||
| 23°C, 50 Hz | 3.40 | 4.50 | ||
| 23°C, 1 kHz | 0.0300 | 0.130 |
| Note Message | |
|---|---|
| 1 . | 60% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™ 5013A | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| Moldex® QS985A/M151 | Mitsubishi Chemical Corporation | Polyolefin, Unspecified | Moldex® |
| UNISOFT TPE™ ST-43A-CL-1-01 | UNITED SOFT PLASTICS, Inc. | SEBS | UNISOFT TPE™ |
| BESTNYL SE35VI02AX | Triesa Plastics | Nylon 66 | BESTNYL |
| Plasmer 1370B/8901 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |