INNOPOL® PP CS 1-3250
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Inno-Comp Ltd. |
| Trademark: | INNOPOL® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | luUlTF_INNOPOL-PP-CS-1-3250.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INNOPOL® CS 1-3250 is a 42 % chalk-filled polypropylene homopolymer compound /PP-H KD42 (ISO 1043)/. INNOPOL® CS 1-3250 is developed for producing injection moulded components for household equipments. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.24 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.5 | g/10 min | ISO 1133 |
| Ash Content (900°C) | 24 | % | ISO 3451-1A |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 25.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 3.6 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 3100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 2.0 | kJ/m² | ISO 179/1eA |
| 23°C | 4.5 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 120 | °C | ISO 75-2/B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Rear Temperature | 190 - 250 | °C | |
| Middle Temperature | 190 - 250 | °C | |
| Front Temperature | 190 - 250 | °C | |
| Processing (Melt) Temp | 230 - 260 | °C | |
| Mold Temperature | 10.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Hold pressure: 30 to 80 % of actual injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 526P | SABIC Americas, Inc. | PP Homopolymer | SABIC® PP |
| ROPOTEN® OB-2-102-3 | LUKOIL Bulgaria Ltd. | LDPE | ROPOTEN® |
| Globalprene® 3537 | Lee Chang Yung Chemical Industry Corp. | SBS | Globalprene® |
| Karina CLEAR PVC COMPOUND -E 57/200-D-AT-IS-SI-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Badaflex® TPU 85A 8046 EX | Bada AG | TPU, Unspecified | Badaflex® |