Ebalta BLH Epoxy 200 / W 400
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | luO2uX_Ebalta-BLH-Epoxy-200-W-400.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Applications
Properties
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Water Absorption | DIN 53495 | ||
| 23°C, 24 hr | 0.11 to 0.13 | % | |
| Saturation, 23°C 1 | 0.29 to 0.33 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 78 to 82 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3000 to 3300 | MPa | ISO 527-2 |
| Tensile Stress | 62.0 to 68.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 8.8 to 9.2 | % | ISO 527-2 |
| Flexural Modulus | 2550 to 2850 | MPa | ISO 178 |
| Flexural Stress | 100 to 120 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 70.0 to 74.0 | °C | ISO 75-2/A |
| Glass Transition Temperature | 80.0 | °C | TMA |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 30 | ||
| Resin | Mix Ratio by Weight: 100 | ||
| Post Cure Time (70°C) | 10 to 12 | hr |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Viscosity (25°C) | 0.25 to 0.41 | Pa·s | |
| Pot Life | |||
| 23°C 2 | 270 to 310 | min | |
| 20°C 3 | 300 to 350 | min | |
| 20°C 4 | 380 to 420 | min |
| Note Message | |
|---|---|
| 1 . | 168 h |
| 2 . | 500 g |
| 3 . | 200 g |
| 4 . | 100 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALCOM® PC 740/4 UV CC1269-08LD | ALBIS PLASTIC GmbH | PC | ALCOM® PC |
| ALCOM® PA6 900/31 FR TCD1 | ALBIS PLASTIC GmbH | Nylon 6 | ALCOM® PA6 |
| Capa™ 6430 | Perstorp Holding AB | PCL | Capa™ |
| GAPEX® FPP40GR16NA | Ferro Corporation | PP Homopolymer | GAPEX® |
| Luran® 378P G7 | Styrolution | SAN | Luran® |