ResMart Utility Nylon 6 6 UVST BLK
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | ResMart |
| Trademark: | ResMart Utility |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ltiw2r_ResMart-Utility-Nylon-6-6-UVST-BLK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unfilled Nylon 6 6, High Impact, Heat and UV Stabilized |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.6 - 2.4 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 44.8 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 10 | % | ASTM D638 |
| Flexural Modulus | 1720 | MPa | ASTM D790 |
| Flexural Strength | 65.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 850 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | No Break | ASTM D256 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 79.4 | °C | |
| Drying Time - Desiccant Dryer | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 277 - 299 | °C | |
| Mold Temperature | 65.6 - 107 | °C | |
| Injection Pressure | 68.9 - 124 | MPa |
| Injection instructions |
|---|
| Dew Point: 0°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nypol® PA B3 HF NTLA010 NT324 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| Arak HDPE I4 | Shazand (Arak) Petrochemical Corporation | HDPE | Arak HDPE |
| Flontech® FT-CAR33-GR2-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| GERMADUR S-5179 GELB | Kunststoff-Kontor-Hamburg GmbH | PBT | GERMADUR |
| Hostacom TRC 483N C12827 | LyondellBasell Industries | PP Copolymer | Hostacom |