RTP 2100 HF TFE 15
| Category: | PEI , Polyether Imide |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ltGrrF_RTP-2100-HF-TFE-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.80 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ASTM D638 |
| Tensile Strength | 82.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 8.0 | % | ASTM D638 |
| Flexural Modulus | 2900 | MPa | ASTM D790 |
| Flexural Strength | 114 | MPa | ASTM D790 |
| Compressive Strength | 110 | MPa | ASTM D695 |
| Coefficient of Friction (With Metal-Dynamic) | 0.15 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 48 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 430 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 207 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 196 | °C | ASTM D648 |
| CLTE - Flow | 5.6E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.22 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.20 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 4.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Additional Information |
|---|
| Wear Factor, K, ASTM D-3702: 65E-10in³/min/ft/lb/hrCoefficient of Friction, Dynamic, ASTM D-3702: 0.15The wear factor and coefficient of friction were both tested on a Falex Model No.6 Wear Testing Machine at 50 FPM, 2000 PV, against C1018 steel of hardness 15-25 Rockwell C, 14-17 micro smoothness. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 343 - 399 | °C | |
| Middle Temperature | 343 - 399 | °C | |
| Front Temperature | 343 - 399 | °C | |
| Mold Temperature | 93.3 - 177 | °C | |
| Injection Pressure | 103 - 138 | MPa | |
| Back Pressure | 0.345 - 0.517 | MPa | |
| Clamp Tonnage | 6.9 - 11 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 211 K | RTP Company | PARA | RTP |
| BESTPOLUX PCG2X/02 | Triesa Plastics | PC | BESTPOLUX |
| ExxonMobil™ PP5341E1 | ExxonMobil Chemical | PP Homopolymer | ExxonMobil™ |
| KOPA® KN333G35CRBK | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| INEOS LDPE 24F564 | INEOS Olefins & Polymers Europe | LDPE | INEOS LDPE |