PRE-ELEC® PP 1397
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lstcG3_PRE-ELEC-PP-1397.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC® PP 1397 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity. PRE-ELEC® PP 1397 has excellent mechanical properties and is easy to extrude. PRE-ELEC® PP 1397 is recommended especially for corrugated sheet. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.969 | g/cm³ | ASTM D792 |
| -- | 0.980 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 1.2 | g/10 min | ISO 1133 |
| 230°C/5.0 kg | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 1.3 - 1.9 | % | ASTM D955 |
| Flow direction | 1.3 - 1.9 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 868 | ||
| Shaw A | 99 | ISO 868 | |
| Shaw D | 74 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Transverse flow : Yield | 22.1 | MPa | ASTM D638 |
| Flow : Yield | 22.8 | MPa | ASTM D638 |
| Transverse flow : Yield | 22.0 | MPa | ISO 527-2 |
| Flow : Yield | 23.0 | MPa | ISO 527-2 |
| Across Flow | 22.8 | MPa | ASTM D638 |
| Flow | 24.8 | MPa | ASTM D638 |
| -- 1 | 23.0 | MPa | ISO 527-2 |
| -- 2 | 25.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Transverse flow : Yield | 16 | % | ISO 527-2 |
| Flow : Yield | 17 | % | ISO 527-2 |
| Fracture 3 | 480 | % | ISO 527-2 |
| Fracture 4 | 500 | % | ISO 527-2 |
| Flexural Modulus | |||
| 4.00 mm | 1380 | MPa | ASTM D790 |
| 4.00 mm | 1400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 5 | |||
| -20°C | 17 | kJ/m² | ASTM D256 |
| -20°C | 18 | kJ/m² | ISO 179 |
| 23°C | 45 | kJ/m² | ISO 179 |
| 23°C | 46 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength 6 | |||
| -20°C | No Break | ASTM D256, ISO 179 | |
| 23°C | No Break | ISO 179, ASTM D256 | |
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 4.00 mm | No Break | ASTM D256 | |
| 23°C, 4.00 mm | No Break | ASTM D256 | |
| Notched Izod Impact 7 | ISO 180 | ||
| -20°C | No Break | ISO 180 | |
| 23°C | No Break | ISO 180 | |
| Unnotched Izod Impact | ASTM D256 | ||
| -20°C, 4.00 mm | No Break | ASTM D256 | |
| 23°C, 4.00 mm | No Break | ASTM D256 | |
| Unnotched Izod Impact Strength 8 | ISO 180 | ||
| -20°C | No Break | ISO 180 | |
| 23°C | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 90.0 | °C | ASTM D648B, ISO 75-2/Bf |
| 1.8 MPa, not annealed | 52.8 | °C | ASTM D648A |
| 1.8 MPa, not annealed | 53.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 150 | °C | ASTM D1525 9 |
| -- | 151 | °C | ISO 306/A50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+4 | ohms | IEC 61340-2-3 |
| Volume Resistivity | < 1.0E+3 | ohms·cm | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Cylinder Zone 1 Temp. | 210 | °C | |
| Cylinder Zone 2 Temp. | 220 | °C | |
| Cylinder Zone 3 Temp. | 220 | °C | |
| Cylinder Zone 4 Temp. | 230 | °C | |
| Cylinder Zone 5 Temp. | 230 | °C |
| Extrusion instructions |
|---|
| Cylinder Zone 6: 230°C |
| Note Message | |
|---|---|
| 1 . | Across Flow |
| 2 . | Flow |
| 3 . | Across Flow |
| 4 . | Flow |
| 5 . | 4 mm thickness |
| 6 . | 4 mm thickness |
| 7 . | 4 mm thickness |
| 8 . | 4 mm thickness |
| 9 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEFTEKHIM PE 5118N (18601) | Nizhnekamskneftekhim Inc. | LLDPE | NEFTEKHIM PE |
| Alpha PVC GW 3042 NATURAL LCF | AlphaGary | PVC, Unspecified | Alpha PVC |
| Appeel® 20D751 | DuPont Packaging & Industrial Polymers | EA | Appeel® |
| Dow ENDURANCE™ DHDA-7708 BK | The Dow Chemical Company | LLDPE | Dow ENDURANCE™ |
| Hydroxy-Purge 30C | InChem Corp. | TP, Unspecified | Hydroxy-Purge |