ACLAR® Rx 160
| Category: | PCTFE , Polychlorotrifluoroethylene |
| Manufacturer: | Honeywell |
| Trademark: | ACLAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lrZYYm_ACLAR-Rx-160.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Aclar Rx 160 is a 0.60 mil CTFE homopolymer high performance barrier film for the pharmaceutical and medical markets. It thermoforms well on conventional blister packaging equipment and offers the benefits of Aclar where barrier considerations are less demanding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.11 | g/cm³ | ASTM D1505 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| MD : 15 µm | 1380 | MPa | ASTM D882 |
| TD : 15 µm | 1290 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 15 µm | 110 | MPa | ASTM D882 |
| TD : Yield, 15 µm | 51.7 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Yield, 15 µm | 100 | % | ASTM D882 |
| TD : Yield, 15 µm | 250 | % | ASTM D882 |
| Water Vapor Transmission Rate | ASTM F1249 | ||
| 15 µm, 40°C, 75% RH | 0.39 | g·mm/m²/atm/24 hr | ASTM F1249 |
| 15 µm, 38°C, 100% RH | 0.42 | g·mm/m²/atm/24 hr | ASTM F1249 |
| 15 µm, 25°C, 60% RH | 0.051 | g·mm/m²/atm/24 hr | ASTM F1249 |
| 15 µm, 30°C, 60% RH | 0.093 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Crystallization Temperature (DSC) | 211 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (15.2 µm) | < 1.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Yield, No Standard: 31.14 m²/kgTensile Strength @ Yld, ASTM D882, MD, 0.6 mil: 12000 to 20000 psiTensile Strength @ Yld, ASTM D882, TD, 0.6 mil: 6000 to 9000 psiTensile Elongation @ Yield, ASTM D882, MD, 0.6 mil: 70 to 130%Tensile Elongation @ Yield, ASTM D882, TD, 0.6 mil: 200 to 300%Secant Modulus, ASTM D882, 0.6 mil, MD: 175000 to 225000Secant Modulus, ASTM D882, 0.6 mil, TD: 170000 to 205000Tear Strength, ASTM D1004, Graves MD: 350 to 400 g/milTear Strength, ASTM D1004, Graves TD: 275 to 325 g/milCrystalline Melting Point, ASTM D4591: 211 °CDimensional Stability, ASTM D1204, MD: +8 to +15 %Dimensional Stability, ASTM D1204, TD: -8 to -13 %All film properties were tested as an average value. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILVER® ABS 350C | Guangdong Silver Age Sci & Tech. Co., Ltd | ABS+PVC | SILVER® |
| Tenogel® ABS A3 HF PRTA010 AB324 MSP | Petropol Industry and Trade of Polymers LTDA | ABS | Tenogel® ABS |
| TEREZ PBT TM 4250 | TER HELL PLASTIC GMBH | PBT | TEREZ PBT |
| ALCOM® LB PC 1000 14073 WT1164-14 | ALBIS PLASTIC GmbH | PC | ALCOM® LB |
| Sylvin 8600-55 Yellow 4166 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |