InnoTuf® TP-4006
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | InnoTuf® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lqxsAA_InnoTuf-TP-4006.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TP-4006 is an impact resistant polyurea formulated for vacuum assisted casting systems and short mold cycle times. Excellent physical properties can be obtained without the utilization of mercury, MOCA, or TDI. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Base Resin | 1.20 | g/cm³ | |
| Cured | 1.21 | g/cm³ | |
| Hardener | 1.24 | g/cm³ | |
| Molding Shrinkage - Flow | 0.20 to 0.50 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1280 | MPa | ASTM D790 |
| Flexural Strength | 58.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 96 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 130 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 63 Mix Ratio by Weight: 65 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time (66°C) | 60 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 38°C 1 | 0.40 | Pa·s | |
| 38°C 2 | 0.50 | Pa·s | |
| 38°C 3 | 1.6 | Pa·s | |
| Curing Time 4 | 25 | hr | |
| Gel Time | 8.0 to 12 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 75 to 85 | ASTM D2240 | |
| Tensile Strength | 65.5 | MPa | ASTM D638 |
| Tensile Elongation at Break | 11 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | Mixed |
| 2 . | Hardener |
| 3 . | Resin |
| 4 . | 1 hour at 150°F + 24 hours at 77°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIBOFORCE® PEEK C2301 | LEIS Polytechnik - polymere Werkstoffe GmbH | PEEK | TRIBOFORCE® |
| Favorite REG100 | Favorite Plastics | PE, Unspecified | Favorite |
| HI-ZEX MILLION™ 145M | Mitsui Chemicals, Inc. | HMWPE | HI-ZEX MILLION™ |
| Sylvin 9048-60 CLEAR | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| PERSTIR® N09K7000AH0 | A.D. Compound S.p.A. | PS (GPPS) | PERSTIR® |