INSULCAST® 333/INSULCURE 11B
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | ITW Polymers Coatings North America |
| Trademark: | INSULCAST® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lqYUv0_INSULCAST-333-INSULCURE-11B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| INSULCAST 333 is a moderate viscosity, self-extinguishing, epoxy potting/casting compound which conforms to the component program of Underwriters Laboratories' Flame Class 94V-O. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore D) | 85 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 82.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.8 | % | ASTM D638 |
| Flexural Strength | 134 | MPa | ASTM D790 |
| Compressive Strength | 100 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| CLTE - Flow | 4.8E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.61 | W/m/K | |
| Heat Deflection Temperature | 155 | °C | |
| Service Temperature | 155 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 17 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 4.50 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 0.020 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 8.0 | ||
| Resin | Mix Ratio by Weight: 100 | ||
| Shelf Life (25°C) | 52 | wk | |
| Post Cure Time (150°C) | 1.0 | hr |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 1 | Amber | ||
| -- 2 | Black | ||
| Density | |||
| -- 3 | 0.948 | g/cm³ | |
| -- 4 | 1.55 | g/cm³ | |
| Viscosity | ASTM D2393 | ||
| 25°C 5 | 0.70 | Pa·s | |
| -- 6 | 3.0 | Pa·s | |
| 25°C 7 | 13 | Pa·s | |
| Curing Time | |||
| 100°C 8 | 2.0 | hr | |
| -- 9 | 4.0 | hr | |
| Pot Life 10(25°C) | 150 | min |
| Note Message | |
|---|---|
| 1 . | INSULCURE 11B |
| 2 . | INSULCAST 333 |
| 3 . | INSULCURE 11B |
| 4 . | INSULCAST 333 |
| 5 . | INSULCURE 11B |
| 6 . | Mixed |
| 7 . | INSULCAST 333 |
| 8 . | for masses less than 1/2 lb. |
| 9 . | 2 hours at 80°C plus 2 hours at 100°C (for masses above 1/2 lb.) |
| 10 . | 100 gram mass |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMTAL PM3009G5 | Polyram Ram-On Industries | Acetal (POM) Copolymer | RAMTAL |
| Wondel® P PM4 | Nanjing Julong Engineering Plastics Co., LTD | PP, Unspecified | Wondel® P |
| Karina GREEN COLOR CONCENTRATE 40/308-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Polifor® E 3 TR/10 NATURALE | SO.F.TER. SPA | PP Copolymer | Polifor® |
| CYCOLAC™ MG38 resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |