Latamid SP1 G/30
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latamid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lpCBEb_Latamid-SP1-G-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyamide 6.10 (PA 6.10). Glass fibres. Low moisture absorption. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.75 to 1.1 | % | |
| Flow : 2.00 mm | 0.35 to 0.65 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 8800 | MPa | |
| 60°C | 6200 | MPa | |
| 90°C | 5300 | MPa | |
| 120°C | 3600 | MPa | |
| 150°C | 3000 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 165 | MPa | |
| Break, 60°C | 120 | MPa | |
| Break, 90°C | 100 | MPa | |
| Break, 120°C | 85.0 | MPa | |
| Break, 150°C | 70.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 3.2 | % | |
| Break, 60°C | 4.2 | % | |
| Break, 90°C | 4.9 | % | |
| Break, 120°C | 5.0 | % | |
| Break, 150°C | 6.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 100 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 140 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 120 | °C | |
| Vicat Softening Temperature | 220 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 8.0E-6 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNO ABS 565L | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| Supol HP190E | LyondellBasell Industries | PP, Unspecified | Supol |
| HiFill FR® HIPS FR | Techmer Engineered Solutions | PS (HIPS) | HiFill FR® |
| Hyundai EP PPF HT960 | HYUNDAI EP Co., Ltd. | PP Homopolymer | Hyundai EP PPF |
| LNP™ STAT-KON™ ME003S compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ STAT-KON™ |