SABIC® PPcompound 2500-6
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lozxzZ_SABIC-PPcompound-2500-6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 2500/6 is a mineral filled modified polypropylene. Typical material properties include very high flow, high impact, good stiffness and low shrinkage and CLTE. Typical material properties also include good chemical resistance and esthetical performance. Typical applications include automotive exterior trims such as lateral siding, bumper strips and bumpers. It can be used in painted and unpainted applications with UV stabilization added on demand. SABIC® PPcompound 2500/6 is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 30 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.80 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5/50 | ||
| Yield, 3.20 mm, Injection Molded | 19.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 15.0 | MPa | |
| Tensile Strain (Break, 3.20 mm, Injection Molded) | > 400 | % | ISO 527-2/5/50 |
| Flexural Modulus 1(Injection Molded) | 1100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | No Break | ISO 179/1eA | |
| Charpy Unnotched Impact Strength (-40°C, Injection Molded) | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength | ISO 180/4A | ||
| -20°C, Injection Molded | 15 | kJ/m² | |
| 0°C, Injection Molded | No Break | ||
| 23°C, Injection Molded | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 90.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 125 | °C | ISO 306/A |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 6.0E-5 | cm/cm/°C | |
| 23 to 80°C | 9.0E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RELENE® 52GF004 | Reliance Industries Limited | HDPE, HMW | RELENE® |
| TEKNIFLEX® COC PG13PG A300 UV | Tekni-Films, a div of Tekni-Plex | Film, PCTFE | TEKNIFLEX® |
| Galloo GP-PP-108 | Galloo Plastics | PP, Unspecified | Galloo |
| PLEXIGLAS® Sheet Soundstop GS CC | Evonik Industries AG | Acrylic (PMMA) | PLEXIGLAS® Sheet |
| TECHNYL® C 246 NATURAL | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |