LNP™ THERMOCOMP™ NF001 compound
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lozNf9_LNP-THERMOCOMP-NF001-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* NF001 is a compound based on PC+ABS resin containing 5% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound PCA-F-1001 Product reorder name: NF001 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.19 | g/cm³ | |
| -- | 1.18 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.30 to 0.50 | % | |
| Across Flow : 24 hr | 0.40 to 0.60 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.17 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.25 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3470 | MPa | ASTM D638 |
| -- | 3300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 63.0 | MPa | ASTM D638 |
| Yield | 62.0 | MPa | ISO 527-2/5 |
| Break 3 | 49.0 | MPa | ASTM D638 |
| Break | 51.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 3.4 | % | ASTM D638 |
| Yield | 3.4 | % | ISO 527-2/5 |
| Break 5 | 6.2 | % | ASTM D638 |
| Break | 5.3 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 3220 | MPa | ASTM D790 |
| -- 7 | 3120 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 94.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 102 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 150 | J/m | ASTM D256 |
| 23°C 9 | 14 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 610 | J/m | ASTM D4812 |
| 23°C 10 | 37 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 34.8 | J | ASTM D3763 |
| -- | 21.7 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 136 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 134 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 123 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 120 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 5.3E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 8.2E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 232 to 243 | °C | |
| Middle Temperature | 249 to 260 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 249 to 271 | °C | |
| Mold Temperature | 37.8 to 82.2 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer F70A | Precision Polymer Engineering Ltd. | Fluoro Si | Precision Polymer |
| Moplen D60P | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| Lucky Enpla LAY1003 | Lucky Enpla Co LTD | PC+ABS | Lucky Enpla |
| tivilon® DP2272/55AF | API SpA | TPV | tivilon® |
| LNP™ VERTON™ RV008ES compound | SABIC Innovative Plastics | Nylon 66 | LNP™ VERTON™ |