Celanex® 2000-3FC
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celanex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lmx6PK_Celanex-2000-3FC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Celanex 2000-3FC is a general purpose, unreinforced PBT with a good balance of mechanical properties and processabillity for use in food contact applications.. Celanex 2000-3FC is a high flow material. Celanex 2000-3FC contains an internal lubricant for improved mold release. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.8 - 2.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 78 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield, 23°C | 57.2 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/1A/50 |
| Fracture, 23°C | 55.8 | MPa | ASTM D638 |
| Tensile Strain | ISO 527-2/1A/50 | ||
| Yield | 4.0 | % | ISO 527-2/1A/50 |
| Fracture | 30 | % | ISO 527-2/1A/50 |
| Flexural Modulus (23°C) | 2600 | MPa | ISO 178 |
| Flexural Stress (23°C) | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 100 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 3.2 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 155 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 55.0 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | |||
| -- | 1.0E+16 | ohms·cm | ASTM D257 |
| -- | 1.0E+17 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| -- 1 | 17 | kV/mm | ASTM D149 |
| -- | 15 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.20 | IEC 60250 | |
| Comparative Tracking Index | > 600 | V | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Hopper Temperature | 20.0 - 50.0 | °C | |
| Rear Temperature | 230 - 240 | °C | |
| Middle Temperature | 235 - 250 | °C | |
| Front Temperature | 235 - 250 | °C | |
| Nozzle Temperature | 250 - 260 | °C | |
| Processing (Melt) Temp | 235 - 260 | °C | |
| Mold Temperature | 65.0 - 93.0 | °C |
| Injection instructions |
|---|
| Manifold Temperature: 250 to 260°CZone 4 Temperature: 240 to 260°CFeed Temperature: 230 to 240°C |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx 15S3304 | The Matrixx Group, Inc. | PP, Unspecified | Matrixx |
| Borealis PP RD204CF | Borealis AG | PP Random Copolymer | Borealis PP |
| Andur 82 DGP | Anderson Development Company | PUR-Ether/TDI | Andur |
| LNP™ LUBRICOMP™ DFL36XXJ compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |
| POLYfill PPH K5040 | Polykemi AB | PP Homopolymer | POLYfill |