Niblan F30 AE/V0
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Soredi S.p.a. |
| Trademark: | Niblan |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lm4eF0_Niblan-F30-AE-V0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT 20% glass fibre reinforced, flame retardant UL officially certified by Underwriter Laboratories (yellow card) as per UL 94 V0 at 1.6 mm rating. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.70 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 to 0.40 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 90 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus 1 | 10000 | MPa | ASTM D790 |
| Flexural Strength 2(Break) | 180 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 215 | °C | ASTM D648 |
| Peak Crystallization Temperature (DSC) | 220 | °C | ASTM D3418 |
| CLTE - Flow (23 to 55°C) | 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Ignition Temperature (2.00 mm) | 960 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 1.3 mm/min |
| 2 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Chemlon® 109 HU | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| EVATHENE® UE647-04 | USI Corporation | EVA | EVATHENE® |
| Lucet® GB-325 | LG Chem Ltd. | Acetal (POM) Copolymer | Lucet® |
| LUVOCOM® 1100-7721/WT9016 | Lehmann & Voss & Co. | PESU | LUVOCOM® |
| PHOENIX™ 6602 | Phon Tech Industrial Company | TPE | PHOENIX™ |