Witcom PA66 10LG
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Witcom Engineering Plastics B.V. |
| Trademark: | Witcom PA66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lkiusO_Witcom-PA66-10LG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Witcom PA66 10LG is a Polyamide 66 (Nylon 66) product filled with 50% long glass fiber. It is available in Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.58 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (3.00 mm) | 0.15 to 0.25 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 4.3 | % | |
| Equilibrium, 23°C, 50% RH | 1.3 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | < 265 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.4 | % | ISO 527-2 |
| Flexural Modulus | 14500 | MPa | ISO 178 |
| Flexural Stress | 420 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 35 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 83 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 253 | °C | ISO 75-2/A |
| CLTE - Flow | 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Imp (3.00 mm) | 105 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | ASTM D257 |
| Comparative Tracking Index | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | ISO 1210 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M1685 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| U-polymer FUN-8000 | UNITIKA Plastics Division | Polyarylate | U-polymer |
| APEX® 3211-65NT | Teknor Apex Company | PVC, Flexible | APEX® |
| KEBATER® PBT BF230 | BARLOG plastics GmbH | PBT | KEBATER® |
| ULTEM™ 2100F resin | SABIC Innovative Plastics Europe | PEI | ULTEM™ |