Formolene FORMAX® L91507E2

Category:	LLDPE , Linear Low Density Polyethylene
Manufacturer:	Formosa Plastics Corporation, U.S.A.
Trademark:	Formolene FORMAX®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	lkQbKW_Formolene-FORMAX-L91507E2.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Formolene FORMAX® L9 is a superior strength linear low density hexene copolymer polyethylene made using a gas-phase process. Film mechanical properties are comparable to premium strength LLDPE film resins.

Formolene FORMAX® L9 is formulated with slip and antiblock for use in high performance film applications offering excellent extrusion processing and outstanding impact strength and tear resistance. Films exhibit good optical properties.

Formolene FORMAX® L9 meets all requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520, covering safe use of polyolefin articles intended for direct food contact.

Suggested Applications:

Industrial Packaging

Industrial Liners

Food Packaging

Can Liners

Consumer Trash Bags

Coextrusion

General Information
Additive	High Antiblock (7000 ppm) 2 High Slip (1500 ppm) 2
Features	Food Contact Acceptable Good Impact Resistance Good Tear Strength Hexene Comonomer High Antiblocking High Slip High Strength Opticals
Uses	Bags Food Packaging Industrial Applications Liners Packaging
Agency Ratings	EC 1907/2006 (REACH) FDA 21 CFR 177.1520
Forms	Pellets
Processing Method	Coextrusion Film Extrusion

Physical	Nominal Value	Unit	Test Method
Density	0.915	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	0.70	g/10 min	ASTM D1238

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	25	µm
Tensile Strength			ASTM D882
MD : Yield, 25 µm, Blown Film	8.45	MPa
TD : Yield, 25 µm, Blown Film	10.5	MPa
MD : Break, 25 µm, Blown Film	39.3	MPa
TD : Break, 25 µm, Blown Film	34.5	MPa
Tensile Elongation			ASTM D882
MD : Break, 25 µm, Blown Film	670	%
TD : Break, 25 µm, Blown Film	880	%
Dart Drop Impact (25 µm, Blown Film)	540	g	ASTM D1709
Elmendorf Tear Strength			ASTM D1922
MD : 25 µm, Blown Film	470	g
TD : 25 µm, Blown Film	650	g
Seal Initiation Temperature ¹(51 µm)	103	°C

Note Message
1 .	Temperature at which 2 lb/in heat seal strengh is achieved. Lako Tool SL-10 Heat Seal/Hot Tack Tester, 0.5 sec dwell, 40 psi bar pressure, peel speed 10 in./min.

Resin Grade	Manufacturer	Category	Trademark
Sipolprene® 35180 W	SIPOL S.p.A	TPC-ET	Sipolprene®
Monprene® OM-12226	Teknor Apex Company	TPE	Monprene®
ALCOM® PA66 910/1 PTFE20	ALBIS PLASTIC GmbH	Nylon 66	ALCOM® PA66
Hylon® N2040MGHL	Ravago Manufacturing Americas, LLC	Nylon 6	Hylon®
Lionpol IM-22018	Lion Polymers Incorporated	TPE	Lionpol