Tenac™-C HC460
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Tenac™-C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | li78iI_Tenac--C-HC460.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Tenac™-C HC460 is an Acetal (POM) Copolymer product. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Tenac™-C HC460 include engineering/industrial parts, automotive and housings. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 1.6 to 2.0 | % | Internal Method |
| Water Absorption (23°C, 24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 88 | ||
| R-Scale | 117 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2750 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Yield | 66.0 | MPa | ISO 527-2 |
| -- | 64.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 40 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2600 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 88.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 7.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | 83 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 163 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 158 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 124 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 102 | °C | ISO 75-2/A |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ASTM D696, ISO 11359-2 |
| Specific Heat | 1470 | J/kg/°C | |
| Thermal Conductivity | 0.23 | W/m/K |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.750 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1002 HI TFE 10 | RTP Company | PBT | RTP |
| Hipolyene 8025 HC | Zylog Plastalloys | TPO (POE) | Hipolyene |
| Petrothene® GA594189 | LyondellBasell Industries | LLDPE | Petrothene® |
| LUVOCOM® 1-VAP 08 | LEHVOSS Group | Nylon 66 | LUVOCOM® |
| NHU-PPS 21110C/F | Zhejiang NHU Comp. Ltd. | PPS | NHU-PPS |