Order Products : sales@su-jiao.com
Leona™ FG171
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Leona™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lhiIKo_Leona-FG171.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Leona™ FG171 is a Polyamide 66 (Nylon 66) product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Typical application: Electrical/Electronic Applications. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.54 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.90 | -- | % | |
| Flow | 0.40 | -- | % | |
| Water Absorption | ||||
| Saturation, 23°C | -- | 0.80 | % | |
| Equilibrium, 23°C, 50% RH | -- | 0.80 | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (M-Scale) | 95 | 55 | ASTM D785, ISO 2039-2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 10200 | 8200 | MPa | ISO 527-2 |
| Tensile Stress | ||||
| Break, 23°C | 154 | 121 | MPa | ISO 527-2 |
| -- | 162 | 127 | MPa | ASTM D638 |
| Tensile Elongation | ||||
| Break | 2.5 | 3.5 | % | ASTM D638 |
| Break, 23°C | 2.5 | 3.0 | % | ISO 527-2 |
| Flexural Modulus | ||||
| -- | 8900 | 7200 | MPa | ASTM D790 |
| 23°C | 9700 | 7900 | MPa | ISO 178 |
| Flexural Strength | ||||
| -- | 256 | 190 | MPa | ASTM D790 |
| 23°C | 244 | 180 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 11 | 12 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 67 | 67 | kJ/m² | ISO 179 |
| Notched Izod Impact | 92 | 110 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 255 | -- | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 256 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | -- | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 240 | -- | °C | ISO 75-2/A |
| CLTE - Flow | 3.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | -- | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | ||||
| -- | 1.0E+15 | -- | ohms·cm | ASTM D257 |
| 23°C | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength | 28 | -- | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index (3.00 mm) | 275 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.750 mm) | V-0 | -- | UL 94 | |
| Glow Wire Flammability Index (3.00 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Star L PA66 30Y D51 | Eurostar Engineering Plastics | Nylon 66 | Star L |
| SUMIKAEXCEL® PES 4100G | Sumitomo Chemical Co., Ltd. | PESU | SUMIKAEXCEL® PES |
| Aaroprene® ATPR 2000 70A | Aaron Industries Corp. | TPE | Aaroprene® |
| EQUATE PE EFDA-7047 | EQUATE Petrochemical Company KSCC | LLDPE | EQUATE PE |
| LNP™ LUBRICOMP™ ZFG26 compound | SABIC Innovative Plastics | PPE+PS | LNP™ LUBRICOMP™ |