Iupiace® GX1210
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupiace® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lhOX5g_Iupiace-GX1210.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Iupiace® GX1210 is a Polyphenylene Ether + PS (PPE+PS) material filled with 35% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Iupiace® GX1210 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.38 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/2.16 kg) | 9.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Across Flow : 3.20 mm | 0.20 to 0.40 | % | |
| Flow : 3.20 mm | 0.10 to 0.30 | % | |
| Water Absorption (Saturation, 23°C) | 0.060 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 10500 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 115 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 10500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 175 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 115 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-1 | ||
| 3.00 mm | 5VB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 280 to 300 | °C | |
| Nozzle Temperature | 280 to 300 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC 6943 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Maxxam™ FR PP301 SHI BK268 | PolyOne Corporation | PP, Unspecified | Maxxam™ FR |
| Nylene® 733 | Custom Resins Group | Nylon 6 | Nylene® |
| Guang Sung PVC GPMA80 | Guang Sung Plastics (GSPL) | PVC, Flexible | Guang Sung PVC |
| ESTOPLAST ZK 6002NN04 | Ester Industries Ltd. | PC | ESTOPLAST ZK |