MarFlex® 5613
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Chevron Phillips Chemical Company LLC |
| Trademark: | MarFlex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lh7uR4_MarFlex-5613.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MarFlex® 5613 is a Low Density Polyethylene material. It is available in Latin America or North America for blown film. Important attributes of MarFlex® 5613 are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 0.48 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 76 | µm | |
| Oxygen Transmission Rate (51 µm, Blown Film) | 3300 | cm³/m²/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate (51 µm, Blown Film) | 10 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Dart Drop Test - Blown Film (50.8 µm) | 65.6 | kN/m | ASTM D1709 |
| Elmendorf Tear Strength 1 | |||
| MD : 50.8 µm | 54.1 | kN/m | ASTM D1922 |
| TD : 50.8 µm | 50.2 | kN/m | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 99.0 | °C | ASTM D1525 |
| Melting Temperature | 111 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 50.8 µm, Blown Film) | 89 | ASTM D2457 | |
| Haze (50.8 µm, Blown Film) | 11 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sup-tech A706SH | Shanghai Suptech Engineering Plastics Co. Ltd. | Nylon, Unspecified | Sup-tech |
| Toraycon® 1200MF | Toray Plastics (Malaysia) Sdn. Bhd. | PBT | Toraycon® |
| BJB Polyurethane TC-891 A/B FR | BJB Enterprises, Inc. | PUR, Unspecified | BJB Polyurethane |
| 3M™ Dyneon™ PTFE Compound FB 01N | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| NORYL™ NH5020 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |