E-FLEX™ I3265
| Category: | EAA , Ethylene Acrylic Acid Copolymer |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | E-FLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lgdmH1_E-FLEX-I3265.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| E-FLEX I3265 is a family of ethylene acrylic acid (E/AA) copolymers, in which part of the acrylic acid is neutralized with Zn/Na ions |
| General Information | |
|---|---|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.948 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 - 20 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 60 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 2.55 26.0 | MPa | ASTM D638 |
| Flexural Modulus 2 | 350 | MPa | ASTM D790 |
| Flexural Strength 3 | 18.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.18 mm | No Break | ASTM D256 | |
| 23°C, 3.18 mm | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 85.0 - 90.0 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 40.0 | °C | |
| Drying Time | 4.0 - 8.0 | hr | |
| Rear Temperature | 180 - 210 | °C | |
| Middle Temperature | 200 - 220 | °C | |
| Front Temperature | 210 - 230 | °C | |
| Nozzle Temperature | 210 - 230 | °C | |
| Mold Temperature | < 30.0 | °C |
| Injection instructions |
|---|
| Injection Speed: 40 to 70%Injection Pressure - 1st: 20 to 50%Injection Pressure - 2nd: 20 to 50%Injection Pressure - Back Pressure: 20 to 50% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 3.0 mm/min |
| 3 . | 3.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NILAMID® B3 GF50 | Nilit Plastics | Nylon 6 | NILAMID® |
| EXCELLOY TK15 | Techno Polymer Co, Ltd. | ABS+PBT | EXCELLOY |
| GAPEX® RPP20EA76BK | Ferro Corporation | PP Homopolymer | GAPEX® |
| Hostacom EKC 330N E1 C12780 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Sylvin 5175-92 White 1472 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |