Tecnoprene® VKM 24 NERO900
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Tecnoprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | lg1822_Tecnoprene-VKM-24-NERO900.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High fluidity polypropylene homopolymer reinforced with 20% chemically coupled talc and 10% glass fiber |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage | 0.60 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Ash Content | 30 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 58.0 | MPa | ASTM D638 |
| Flexural Modulus | 4200 | MPa | ASTM D790 |
| Flexural Strength | 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.3 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 60 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 136 | °C | ASTM D648 |
| CLTE - Flow | 6.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
| Dielectric Constant (1 kHz) | 2.50 | ASTM D150 | |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 190 | °C | |
| Middle Temperature | 210 | °C | |
| Front Temperature | 230 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx FPP5A20CC | The Matrixx Group, Inc. | PP, Unspecified | Matrixx |
| TEKAMID™ TA210ST | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| Telcar® TL-1444A | Teknor Apex Company | TPE | Telcar® |
| Borealis PE FA5224 | Borealis AG | LDPE | Borealis PE |
| APEX® 90-R471U-85-NT | Teknor Apex Company | PVC, Flexible | APEX® |